You can't run an 8 atom system without k-points, it doesn't make sense and you can't run hybrid functionals with k-points at the moment.<div><br></div><div>Absolute minimum is a 64 atom system (still nowhere near converged). For the HSE screened exchange, I'd suggest you wil need box dimensions of _at least_ 1 nm on each side otherwise strange things will happen. </div><div><br></div><div>If ADMM is working well the extra cost of going to bigger systems will not be too big. Plane wave code will be more efficient for the smallest cells, but CP2K should win out for bigger defect cells.</div><div><br></div><div>Matt<br><br></div><div class="gmail_quote"><div dir="auto" class="gmail_attr">On Friday, April 9, 2021 at 9:47:52 AM UTC+1 ma...@gmail.com wrote:<br/></div><blockquote class="gmail_quote" style="margin: 0 0 0 0.8ex; border-left: 1px solid rgb(204, 204, 204); padding-left: 1ex;">Hi,<div><br></div><div>I'm a beginner of using cp2k7.1. My aim is to use HSE06 to calculate the Si (8 atoms) system. However the calculating speed is extremly slow. I used OT and ADMM approaches and GAMMA point with 48 cores, but this CELL_OPT calculation took around 30 mins to finish. As a comparison, I used VASP to run the same geometry with HSE06 and with only 1 core, the calculation finished in 50 seconds... So clearly, I must did something wrong in the input file resulting in a significant limitation in the calculating speed but I couldn't figure out which part is wrong. Could somebody please provide some help? Thanks.</div><div><br></div><div>Regards,</div><div>Hongyang</div></blockquote></div>